Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD955 | 0.37 % |
| Water absorption rate | | ASTMD570 | 0.060 % |
| density | | ASTMD792 | 1.89 g/cm³ |
| Apparent density | | ASTMD1895 | 0.89 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 54 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Limiting Oxygen Index | | ASTMD2863 | 41 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | ASTMD695 | 119 MPa |
| Tensile modulus | | ASTMD638 | 11700 MPa |
| tensile strength | | ASTMD638 | 64.0 MPa |
| elongation | Break | ASTMD638 | 1.1 % |
| Flexural modulus | | ASTMD790 | 10300 MPa |
| bending strength | | ASTMD790 | 101 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ASTMD256 | 35.1 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 42 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1.9E+15 ohms·cm |
| dielectric strength | | ASTMD149 | 13 kV/mm |
| dielectric strength | | ASTMD149 | 11 kV/mm |
| Dissipation Factor | | ASTMD150 | 0.017 |
| arc resistance | | ASTMD495 | 189 sec |
| dielectric constant | | ASTMD150 | 4.40 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | ASTMD794 | 217 °C |
| | ASTME831 | 8.6E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.87 W/m/K |
| | ASTMD648 | 253 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare