Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.80 g/cm³ |
| Melt volume flow rate | | ISO1133 | 30.0 cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.90 % |
| Shrinkage rate | | ISO294-4 | 0.20 % |
| Shrinkage rate | | ISO294-4 | 0.30 % |
| Shrinkage rate | | ISO294-4 | 0.10 % |
| Water absorption rate | | ISO62 | 0.30 % |
| Water absorption rate | | ISO62 | 0.10 % |
| | ISO1628 | 91.0 ml/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 200 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 750 °C |
| Extreme Oxygen Index 12 | | ISO4589-2 | 21 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ElectrolyticalCorrosion | | IEC60426 | A1 |
| ISO Shortcut | | ISO7792 | PBT+PET,GHLMR,09-100,GF30 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178/A | 10300 Mpa |
| bending strength | | ASTMD790 | 207 Mpa |
| Bending stress | | ISO178 | 230 Mpa |
| | | 3.0 % |
| Tensile modulus | | ASTMD638 | 9980 Mpa |
| Tensile modulus | | ISO527-2/1 | 10400 Mpa |
| tensile strength | | ASTMD638 | 123 Mpa |
| Tensile stress | | ISO527-2/5 | 145 Mpa |
| elongation | | ASTMD638 | 2.5 % |
| Tensile strain | | ISO527-2/5 | 2.8 % |
| TensileCreepModule | | ISO899-1 | 10000 Mpa |
| Tensile creep modulus | | ISO899-1 | 8500 Mpa |
| Flexural modulus | | ASTMD790 | 8550 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 55 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 65 kJ/m² |
| | ISO180/1U | 55 kJ/m² |
| | ISO180/1U | 55 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|
| FilmPunctureEnergy6 | | ISO6603-2 | 2.10 J |
| Membrane piercing force 6 | | ISO6603-2 | 650 N |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 27 KV/mm |
| | IEC60250 | 4.00 |
| | IEC60250 | 3.80 |
| CTI | | IEC60112 | 250 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| TemperatureIndex11 | | IEC60216 | 155 |
| TemperatureIndex11 | | IEC60216 | 140 |
| TemperatureIndex11 | | IEC60216 | 155 |
| Melting temperature 7 | | ISO11357-3 | 225to250 °C |
| | ISO11359-2 | 3E-05 cm/cm/°C |
| | ISO11359-2 | 6E-05 cm/cm/°C |
| thermal conductivity | | ISO8302 | 0.27 W/m/K |
| RTI Elec | | UL746 | 140 °C |
| RTI Imp | | UL746 | 125 °C |
| RTI Str | | UL746 | 140 °C |
| Half Interval | | IEC60216 | 13.5 °C |
| Half Interval | | IEC60216 | 10.2 °C |
| Half Interval | | IEC60216 | 10.2 °C |
| | ISO75-2/B | 220 °C |
| | ISO75-2/A | 200 °C |
| vicat | | ISO306/B120 | 205 °C |
| BallPressure Test | | IEC60695-10-2 | Pass |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.