'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT/PET T7331 COVESTRO GERMANY
611
- Unit Price:US$ 2,667 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:53MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Easy to form｜High impact
- Application Areas:Automotive Applications｜Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 | kJ/m² |
| -30°C | ISO 180/1U | 55 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 55 | kJ/m² |
| 23°C | ISO 179/1eU | 65 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 750 | °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB | |
| 0.8mm | UL 94 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 21 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | 23°C | ISO 178/A | 10300 | Mpa |
| bending strength | 23°C | ASTM D790 | 207 | Mpa |
| 23°C | ISO 178 | 230 | Mpa | |
| Bending strain | 23°C | 3.0 | % | |
| Tensile modulus | 23°C | ASTM D638 | 9980 | Mpa |
| 23°C | ISO 527-2/1 | 10400 | Mpa | |
| tensile strength | Break,23°C | ASTM D638 | 123 | Mpa |
| Break,23°C | ISO 527-2/5 | 145 | Mpa | |
| elongation | Break,23°C | ASTM D638 | 2.5 | % |
| Tensile strain | Break,23°C | ISO 527-2/5 | 2.8 | % |
| Tensile creep modulus | 1hr | ISO 899-1 | 10000 | Mpa |
| 1000hr | ISO 899-1 | 8500 | Mpa | |
| Bending modulus | 23°C | ASTM D790 | 8550 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Half Interval | --10 | IEC 60216 | 10.2 | °C |
| --9 | IEC 60216 | 10.2 | °C | |
| RTI Elec | UL 746 | 140 | °C | |
| thermal conductivity | 23°C | ISO 8302 | 0.27 | W/m/K |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6E-05 | cm/cm/°C |
| MD：23to55°C | ISO 11359-2 | 3E-05 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 225to250 | °C | |
| TemperatureIndex | 抗张强度 | IEC 60216 | 155 | |
| 拉伸冲击强度 | IEC 60216 | 140 | ||
| 介电强度 | IEC 60216 | 155 | ||
| Half Interval | --8 | IEC 60216 | 13.5 | °C |
| RTI Str | UL 746 | 140 | °C | |
| RTI Imp | UL 746 | 125 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 200 | °C | |
| Vicat softening temperature | ISO 306/B120 | 205 | °C | |
| Ball Pressure Test | 220°C | IEC 60695-10-2 | Pass | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD:270°C,2.00mm2 | ISO 294-4 | 0.30 | % |
| TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.20 | % | |
| TD:270°C,2.00mm2 | ISO 294-4 | 0.90 | % | |
| Melt Volume Flow Rate (MVR) | 260°C/5.0kg | ISO 1133 | 30.0 | cm3/10min |
| Apparent density | ISO 60 | 0.80 | g/cm³ | |
| Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 | % |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.10 | % | |
| Viscosity value | 降低的粘度 | ISO 1628 | 91.0 | ml/g |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Compared to the anti leakage trace index | SolutionA | IEC 60112 | PLC 2 | |
| Relative permittivity | 23°C,1MHz | IEC 60250 | 3.80 | |
| 23°C,100Hz | IEC 60250 | 4.00 | ||
| Dielectric strength | 23°C,1.00mm | IEC 60243-1 | 27 | KV/mm |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Ball Pressure Test | ISO 2039-1 | 200 | Mpa | |
| film | Test Condition | Test Method | Test Result | Test Unit |
| Thin film puncture strength | ISO 6603-2 | 2.10 | J | |
| ISO 6603-2 | 650 | N | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Electrolytic corrosion | IEC 60426 | A1 | ||
| ISO Shortcut | ISO 7792 | PBT+PET.GHLMR.09-100.GF30 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.