Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.41 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 27 g/10min |
| Shrinkage rate | | ASTM D955 | 2.0 % |
| Water absorption rate | | ASTM D570 | 0.22 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 59 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 60.0 MPa |
| elongation | | ASTM D638 | 40 % |
| Flexural modulus | | ASTM D790 | 2560 MPa |
| bending strength | | ASTM D790 | 83.0 MPa |
| shear strength | | ASTM D732 | 55.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1E+11 ohms |
| Volume resistivity | | ASTM D257 | 1E+10 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 158 °C |
| Heat distortion temperature | | ASTM D648 | 110 °C |
| Heat distortion temperature | Melting Temperature | ASTM D648 | 165 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.