| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.85到1.95 g/cm³ |
| Apparent density | | ISO60 | 0.60到0.80 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.30到0.50 % |
| Water absorption rate | | ISO62 | <0.20 % |
| PostShrinkage | | ISO2577 | <0.050 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 960 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >20.0 MPa |
| CompressionMoldingTemperature | | | 165到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ISO527-2 | 7000到9000 MPa |
| Tensile stress | | ISO527-2 | 70.0到90.0 MPa |
| Tensile stress | Injection | ISO527-2 | 100到120 MPa |
| Flexural modulus | Compression Molded | ISO178 | 16000到18000 MPa |
| Flexural modulus | Injection | ISO178 | 18000到22000 MPa |
| Tensile modulus | Compression Molded | ISO527-2 | 7000到9000 MPa |
| Bending stress | Compression Molded | ISO178 | 120到140 MPa |
| Bending stress | Injection | ISO178 | 200到220 MPa |
| compression stress | | ISO604 | 250到300 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 2.0到3.0 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 3.0到5.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 6.0到8.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 10到12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1.0E+12到1.0E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 20到30 kV/mm |
| | IEC60250 | 6.008.00 |
| | IEC60250 | 4.006.00 |
| Dissipation Factor | | IEC60250 | 0.10到0.20 |
| Dissipation Factor | | IEC60250 | 0.020到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | >175 V |
| Surface Resistivity | | IEC60093 | 1.0E+10到1.0E+11 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| maximum service temperature | | IEC60216 | 150 °C |
| | ISO75-2/A | >200 °C |
| | ISO75-2/C | 160到180 °C |
| | ISO11359-2 | 1.5E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40到0.60 W/m/K |
| maximum service temperature | | IEC60216 | 230 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.