Phenolic RESINOL® EPF 400 RASCHIG GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Supplementary InformationTest ConditionTest MethodRASCHIG GmbH/RESINOL® EPF 400
Compression molding pressure>20.0 MPa
Compression molding temperature165to180 °C
thermal performanceTest ConditionTest MethodRASCHIG GmbH/RESINOL® EPF 400
Hot deformation temperature8.0MPa,UnannealedISO 75-2/C160to180 °C
1.8MPa,UnannealedISO 75-2/A>200 °C
Linear coefficient of thermal expansionMD：50to150°CISO 11359-21.5E-5到2.0E-5 cm/cm/°C
Maximum operating temperature20,000hIEC 60216150 °C
<50hIEC 60216230 °C
thermal conductivityASTME14610.40to0.60 W/m/K
mechanical propertiesTest ConditionTest MethodRASCHIG GmbH/RESINOL® EPF 400
Bending modulusInjectionISO 17818000to22000 MPa
Compression MoldedISO 17816000to18000 MPa
bending strengthInjectionISO 178200to220 MPa
Compression MoldedISO 178120to140 MPa
Compressive stressISO 604250to300 MPa
Tensile modulusCompression MoldedISO 527-27000to9000 MPa
InjectionISO 527-27000to9000 MPa
tensile strengthCompressionMoldedISO 527-270.0to90.0 MPa
InjectionISO 527-2100to120 MPa
Electrical performanceTest ConditionTest MethodRASCHIG GmbH/RESINOL® EPF 400
Arc resistanceASTM D495PLC 4
Compared to the anti leakage trace indexIEC 60112PLC 3
Dielectric strengthIEC 60243-120to30 kV/mm
Dissipation factor1MHzIEC 602500.020to0.030
100HzIEC 602500.10to0.20
Relative permittivity100HzIEC 602506.008.00
1MHzIEC 602504.006.00
Surface resistivityIEC 600931.0E+10到1.0E+11 ohms
Volume resistivityIEC 600931.0E+12到1.0E+13 ohms·cm
Physical propertiesTest ConditionTest MethodRASCHIG GmbH/RESINOL® EPF 400
Apparent densityISO 600.60to0.80 g/cm³
densityISO 11831.85to1.95 g/cm³
Shrinkage rateISO 2577<0.050 %
MD2ISO 25770.30to0.50 %
Water absorption rate23°C,24hrISO 62<0.20 %
impact performanceTest ConditionTest MethodRASCHIG GmbH/RESINOL® EPF 400
Charpy Notched Impact StrengthInjectionISO 179/1eA3.0to5.0 kJ/m²
Compression MoldedISO 179/1eA2.0to3.0 kJ/m²
Impact strength of simply supported beam without notchInjectionISO 179/1eU10to12 kJ/m²
Compression MoldedISO 179/1eU6.0to8.0 kJ/m²
flammabilityTest ConditionTest MethodRASCHIG GmbH/RESINOL® EPF 400
Burning wire flammability indexIEC 60695-2-12960 °C
Hot filament ignition temperatureIEC 60695-2-13960 °C
UL flame retardant rating1.5mmUL 94V-0