PC PANLITE® MN-3600H
29
- Properties:heat-resistingFlame retardantGood impact resistanceGood liquidityHalogen-free
- Usages:Electrical fieldElectronic fieldAutomotive sector
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO1133 | 17.5 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50to0.70 % | |
| 内部方法 | 0.50to0.70 % | ||
| Water absorption rate | ISO62 | 0.22 % |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 以上加工数据，为参考值.以生产厂商设备的实际状况而进行调整 | ||
| 抗撞击性良好、耐热性高、良好的流动性、无卤、阻燃性能 | |||
| colour | 不透明 | ||
| purpose | 电气/电子应用领域、汽车领域的应用 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | IEC60695-2-12 | 930 °C | |
| Hot filament ignition temperature | IEC60695-2-13 | 875 °C | |
| IEC60695-2-13 | 825 °C | ||
| IEC60695-2-13 | 825 °C | ||
| IEC60695-2-13 | 825 °C | ||
| UL flame retardant rating | UL94 | HB | |
| UL94 | V-1 | ||
| UL94 | V-0 | ||
| UL94 | 5VB | ||
| UL94 | 5VA | ||
| Burning wire flammability index | IEC60695-2-12 | 960 °C | |
| IEC60695-2-12 | 930 °C | ||
| IEC60695-2-12 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638/ISO 527 | 2350 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 60.0 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 7.0 % | |
| Flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 95.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 100 % | |
| Bending modulus 2 | ISO178 | 2300 Mpa | |
| Bending stress 2 | ISO178 | 95.0 Mpa | |
| Tensile modulus | ISO527-2/1 | 2350 Mpa | |
| Tensile stress | ISO527-2/50 | 60.0 Mpa | |
| ISO527-2/50 | 50.0 Mpa | ||
| Tensile strain | ISO527-2/50 | 7.0 % | |
| ISO527-2/50 | 100 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Mold Shrinkage | ASTM D955 | 0.50-0.70 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.22 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTM D648/ISO 75 | 125 ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000070 mm/mm.℃ | |
| RTI Str | UL746 | 95.0 °C | |
| ISO75-2/B | 125 °C | ||
| ISO75-2/A | 112 °C | ||
| ISO11359-2 | 7E-05 cm/cm/°C | ||
| ISO11359-2 | 7E-05 cm/cm/°C | ||
| RTI Elec | UL746 | 95.0 °C | |
| RTI Imp | UL746 | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.