Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC MN-3600H TEIJIN JAPAN
PANLITE®
Electrical field、Electronic field、Automotive sector
heat-resisting、Flame retardant、Good impact resistance、Good liquidity、Halogen-free
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 95.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2/1 | 2350 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 7.0 % | |
| elongation at break | ASTM D638/ISO 527 | 100 % | |
| tensile strength | ASTM D638/ISO 527 | 60.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 屈服 | ISO 527-2/50 | 7.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| 屈服 | ISO 527-2/50 | 60.0 Mpa | |
| bending strength | ISO 178 | 95.0 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 2350 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| other | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| characteristic | 抗撞击性良好、耐热性高、良好的流动性、无卤、阻燃性能 | ||
| notes | 以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整 | ||
| Color | 不透明 | ||
| purpose | 电气/电子应用领域、汽车领域的应用 |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.50-0.70 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.22 % |
| flammability | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| UL flame retardant rating | 0.45mm | UL 94 | HB |
| 3.0mm | UL 94 | 5VA | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 825 °C |
| 1.0mm | IEC 60695-2-13 | 875 °C | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| 3.0mm | IEC 60695-2-12 | 930 °C | |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | 2.0mm | UL 94 | 5VB |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 930 °C |
| UL flame retardant rating | 1.0mm | UL 94 | V-1 |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 825 °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 17.5 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.22 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.50-0.70 % |
| TD:4.00mm | 内部方法 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 125 ℃（℉） |
| RTI Imp | 1.5mm | UL 746 | 95.0 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 125 °C |
| RTI Str | 1.5mm | UL 746 | 95.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 112 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI Elec | 1.5mm | UL 746 | 95.0 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | 0.000070 mm/mm.℃ |