| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 熔体体积流动速率 | 300°C/10.0kg | ISO1133 | 49.0 cm3/10min |
| 收缩率 | MD:24小时 | ASTMD955 | 0.33 % |
| 收缩率 | TD:24小时 | ASTMD955 | 0.48 % |
| 23°C,24hr | | 内部方法 | 0.25 % |
| 平衡,23°C,50%RH | | ISO62 | 0.040 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 199 °C |
| 线性热膨胀系数 | MD:-40到40°C | ASTME831 | 3.1E-05 cm/cm/°C |
| 线性热膨胀系数 | MD:40到120°C | ASTME831 | 1.9E-05 cm/cm/°C |
| 线性热膨胀系数 | TD:-40到40°C | ASTME831 | 4.6E-05 cm/cm/°C |
| 线性热膨胀系数 | TD:40到120°C | ASTME831 | 7E-05 cm/cm/°C |
| 比热 | | ASTMC351 | 1420 J/kg/°C |
| --6 | | ASTM D790/ISO 178 | 1.2 W/m/K |
| --7 | | ASTM D790/ISO 178 | 2.1 W/m/K |
| --8 | | ISO22007-2 | 0.99 W/m/K |
| --9 | | ISO22007-2 | 1.4 W/m/K |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | 1.00mm | UL94 | V-0 |
| 灼热丝易燃指数 | 2.00mm | IEC60695-2-12 | 960 °C |
| 热灯丝点火温度 | 1.00mm | IEC60695-2-13 | 775 °C |
| 热灯丝点火温度 | 3.00mm | IEC60695-2-13 | 850 °C |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| 热丝引燃(HWI) | HWI | UL746 | PLC 0 |
| 表面电阻率 | | ASTMD257 | >1.0E+15 ohms |
| 介电强度 | 1.00mm,inOil | ASTMD149 | >10 KV/mm |
| 介电常数 | 1.10GHz | ASTMES7-83 | 4.74 |
| 耗散因数 | 1.10GHz | ASTMES7-83 | 7.7E-03 |
| 漏电起痕指数 | | IEC60112 | 600 V |
| 高电弧燃烧指数(HAI) | HAI | UL746 | PLC 0 |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸模量1 | | ASTMD638 | 7240 Mpa |
| 抗张强度 | 断裂 | ASTMD638 | 52.0 Mpa |
| 伸长率 | 断裂 | ASTMD638 | 2.0 % |
| 弯曲模量 | 50.0mm跨距 | ASTMD790 | 9050 Mpa |
| 弯曲强度5 | 断裂,50.0mm跨距 | ASTMD790 | 76.0 Mpa |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 简支梁无缺口冲击强度 | | ISO179 | 5.3到18 kJ/m² |
| 悬壁梁无缺口冲击强度 | 23°C | ASTMD4812 | 180 J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.