Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 PX11311-WH9F059 SABIC INNOVATIVE US
LNP™ KONDUIT™
Automotive body panels、Automotive sector
Dimensional stability、Low Specific Gravity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311-WH9F059 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 5.3to18 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 180 J/m |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311-WH9F059 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Dissipation Factor | 1.10GHz | ASTMES7-83 | 7.7E-03 |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| dielectric strength | 1.00mm,inOil | ASTM D149 | >10 KV/mm |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| dielectric constant | 1.10GHz | ASTMES7-83 | 4.74 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311-WH9F059 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 7240 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.0 % |
| tensile strength | 断裂 | ASTM D638 | 52.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 9050 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 76.0 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311-WH9F059 |
|---|---|---|---|
| Burning wire flammability index | 2.00mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.00mm | UL 94 | V-0 |
| Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 850 °C |
| 1.00mm | IEC 60695-2-13 | 775 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311-WH9F059 |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.48 % |
| Melt volume flow rate | 300°C/10.0kg | ISO 1133 | 49.0 cm3/10min |
| Shrinkage rate | MD:24小时 | ASTM D955 | 0.33 % |
| Balance, 23 ° C, 50% RH | ISO 62 | 0.040 % | |
| 23°C,24hr | 内部方法 | 0.25 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311-WH9F059 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 199 °C |
| --9 | ISO 22007-2 | 1.4 W/m/K | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 4.6E-05 cm/cm/°C |
| TD:40到120°C | ASTME831 | 7E-05 cm/cm/°C | |
| --6 | ASTM D790/ISO 178 | 1.2 W/m/K | |
| --7 | ASTM D790/ISO 178 | 2.1 W/m/K | |
| --8 | ISO 22007-2 | 0.99 W/m/K | |
| Linear coefficient of thermal expansion | MD:40到120°C | ASTME831 | 1.9E-05 cm/cm/°C |
| specific heat | ASTMC351 | 1420 J/kg/°C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 3.1E-05 cm/cm/°C |