Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.32 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.0 g/10min |
| Shrinkage rate | | ASTM D955 | 0.80to1.0 % |
| Shrinkage rate | | ASTM D955 | 1.2to1.4 % |
| Water absorption rate | | ASTM D570 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 40 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | ASTM D695 | 112 MPa |
| shear strength | | ASTM D732 | 79.0 MPa |
| Tensile modulus | | ASTM D638 | 3700 MPa |
| Tensile modulus | | ISO 527-2/1A/1 | 3900 MPa |
| tensile strength | Yield | ISO 527-2/1A/50 | 91.0 MPa |
| Poisson's ratio | | ASTME132 | 0.43 |
| elongation | | ASTM D638 | 5.0 % |
| elongation | Yield | ISO 527-2/1A/50 | 4.5 % |
| elongation | | ASTM D638 | 25 % |
| elongation | Break | ISO 527-2/1A/50 | 25 % |
| Flexural modulus | | ASTM D790 | 3700 MPa |
| Flexural modulus | | ISO 178 | 3800 MPa |
| bending strength | | ASTM D790 | 141 MPa |
| bending strength | | ISO 178 | 138 MPa |
| tensile strength | | ASTM D638 | 89.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 80 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 7.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTMD4812 | 无断裂 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | | 450 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 19 kV/mm |
| dielectric constant | | ASTM D150 | 3.12 |
| dielectric constant | | ASTM D150 | 3.06 |
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Dissipation Factor | | ASTM D150 | 4E-03 |
| Surface Resistivity | | ASTM D257 | >1.9E+17 ohms |
| Volume resistivity | | ASTM D257 | 3.1E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 170 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ASTM D3418 | 150 °C |
| melting temperature | | ASTM D3418 | 340 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 4.5E-05 cm/cm/°C |
| specific heat | | DSC | 1410 J/kg/°C |
| specific heat | | DSC | 1970 J/kg/°C |
| Heat distortion temperature | | ASTM D648 | 161 °C |
| thermal conductivity | | ASTME1530 | 0.22 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.