PP-R TOPILENE® B240P HYOSUNG KOREA
106
- Properties:High rigidity
- Usages:PPR tube
Compare
View PricesTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-792 | 0.91 g/cm | |
| melt mass-flow rate | ASTM D-1238 | 0.4 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D-256 | 无破损 kg.cm/cm | |
| Flexural modulus | ASTM D-790 | 11500 kg/cm | |
| Impact strength of cantilever beam gap | ASTM D-256 | 6 kg.cm/cm | |
| elongation at break | ASTM D-638 | 500 % | |
| tensile strength | ASTM D-638 | 270 kg/cm | |
| ASTM D-638 | 240 kg/cm | ||
| Impact strength of cantilever beam gap | ASTM D-256 | 10 kg.cm/cm | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 12 kg·cm/cm(J/M)ft·lb/in | |
| Rockwell hardness | ASTM D785 | 90 | |
| elongation at break | ASTM D638/ISO 527 | 200 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | HS Method | >10 Ω |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 0.4 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | Dilatometor | 1.5×10 K | |
| vicat | ASTM D-1525 | 150 °C | |
| melting temperature | HS Method | 162 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.