PA66/PTFE LNP™ LUBRICOMP™ RFL-4033 SABIC INNOVATIVE US
93
- Properties:wear resistantenhance
- Usages:Electrical appliancesElectronic and Electrical Applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 0.50to0.70 % | |
| ASTMD955 | 1.6to1.8 % | ||
| ISO294-4 | 1.7 % | ||
| ISO294-4 | 0.64 % | ||
| Water absorption rate | ASTMD570 | 0.60 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO178 | 5800 Mpa | |
| bending strength | ASTMD790 | 179 Mpa | |
| Bending stress | ISO178 | 183 Mpa | |
| ASTMD3702Modified | 0.40 | ||
| ASTMD3702Modified | 0.45 | ||
| Wear factor - Washer | ASTMD3702Modified | 19.5 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ASTMD638 | 6890 Mpa | |
| ISO527-2/1 | 6440 Mpa | ||
| tensile strength | ASTMD638 | 120 Mpa | |
| Tensile stress | ISO527-2 | 118 Mpa | |
| tensile strength | ASTMD638 | 120 Mpa | |
| Tensile stress | ISO527-2 | 118 Mpa | |
| elongation | ASTMD638 | 3.1 % | |
| Tensile strain | ISO527-2 | 3.1 % | |
| elongation | ASTMD638 | 3.1 % | |
| Tensile strain | ISO527-2 | 3.1 % | |
| Flexural modulus | ASTMD790 | 5520 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | ISO180/1A | 6.7 kJ/m² | |
| UnnotchedIzodImpactStrength3 | ISO180/1U | 35 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 7.60 J | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 2.10 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 261 °C | ||
| Hot deformation temperature 4 | ISO75-2/Bf | 260 °C | |
| ASTMD648 | 247 °C | ||
| Hot deformation temperature 4 | ISO75-2/Af | 243 °C | |
| ASTME831 | 8.3E-05 cm/cm/°C | ||
| ISO11359-2 | 8.3E-05 cm/cm/°C | ||
| ASTME831 | 4E-05 cm/cm/°C | ||
| ISO11359-2 | 3.9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.