Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66/PTFE RFL-4033 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Electronic and Electrical
wear resistant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 35 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.10 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.7 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 7.60 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 6440 Mpa | |
| elongation | 屈服 | ASTM D638 | 3.1 % |
| bending strength | ASTM D790 | 179 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 3.1 % |
| Wear factor | Washer | ASTM D3702Modified | 19.5 10^-10in^5-min/ft-lb-hr |
| tensile strength | 断裂 | ASTM D638 | 120 Mpa |
| 断裂 | ISO 527-2 | 118 Mpa | |
| Flexural modulus | ASTM D790 | 5520 Mpa | |
| Tensile modulus | ASTM D638 | 6890 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.1 % |
| bending strength | ISO 178 | 183 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.45 |
| Flexural modulus | ISO 178 | 5800 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.1 % |
| tensile strength | 屈服 | ASTM D638 | 120 Mpa |
| 屈服 | ISO 527-2 | 118 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.40 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.64 % |
| MD：24小时 | ASTM D955 | 0.50-0.70 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.60 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 1.6-1.8 % |
| TD:24小时 | ISO 294-4 | 1.7 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RFL-4033 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 260 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 4E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 3.9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 261 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8.3E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 8.3E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 243 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 247 °C |