Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
melt mass-flow rate | | ASTM D1238 | 14to45 g/10min |
melt mass-flow rate | | ISO 1133 | 19to40 g/10min |
Melt volume flow rate | | ISO 1133 | 17.0to26.0 cm³/10min |
Shrinkage rate | | ASTM D955 | 0.50to0.60 % |
Shrinkage rate | | ISO 294-4 | 0.59to0.70 % |
Water absorption rate | | ASTM D570 | 0.10to0.25 % |
Water absorption rate | | ISO 62 | 0.60to1.0 % |
Water absorption rate | | ISO 62 | 0.20to0.30 % |
density | | ASTM D792 | 1.10to1.25 g/cm³ |
density | | ISO 1183 | 1.11to1.20 g/cm³ |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 109to116 |
ball-indentation hardness | | ISO 2039-1 | 88.7to110 MPa |
flammability | Test Condition | Test Method | Test Result |
---|
Hot filament ignition temperature | | IEC 60695-2-13 | 550to960 °C |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ASTM D638 | 44.0to66.0 MPa |
tensile strength | | ISO 527-2 | 39.0to64.3 MPa |
elongation | | ASTM D638 | 3.7to6.1 % |
elongation | | ISO 527-2 | 2.3to8.7 % |
elongation | | ASTM D638 | 23to100 % |
elongation | | ISO 527-2 | 36to80 % |
Flexural modulus | | ASTM D790 | 2080to2770 MPa |
Flexural modulus | | ISO 178 | 2000to2640 MPa |
bending strength | | ASTM D790 | 68.0to94.0 MPa |
bending strength | | ISO 178 | 72.8to97.5 MPa |
bending strength | | ASTM D790 | 81.7to95.4 MPa |
Tensile modulus | | ASTM D638 | 2540to2720 MPa |
Tensile modulus | | ISO 527-2 | 2120to2760 MPa |
tensile strength | | ASTM D638 | 52.9to65.6 MPa |
tensile strength | | ISO 527-2 | 54.6to62.4 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Charpy Notched Impact Strength | | ISO 179 | 5.0to62 kJ/m² |
Impact strength of cantilever beam gap | | ASTM D256 | 140to600 J/m |
Impact strength of cantilever beam gap | | ISO 180 | 16to61 kJ/m² |
Dart impact | | ASTM D3763 | 35.3to47.9 J |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | IEC 60093 | 1.0E+13到1.0E+15 ohms |
Volume resistivity | | IEC 60093 | 1.0E+13到1.0E+15 ohms·cm |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | ASTME831 | 7.2E-5到7.3E-5 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 1.0E-5到8.6E-5 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 7.2E-5到7.9E-5 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 7.1E-5到7.8E-5 cm/cm/°C |
Heat distortion temperature | | ASTM D648 | 102to130 °C |
Heat distortion temperature | | ISO 75-2/B | 98.4to132 °C |
Heat distortion temperature | | ASTM D648 | 87.7to113 °C |
Heat distortion temperature | | ISO 75-2/A | 87.2to122 °C |
vicat | | ASTM D1525 | 104to138 °C |
vicat | | ISO 306 | 102to139 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.