ASA+PC Generic ASA+PC Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Generic/Generic ASA+PC |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.0to62 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 140to600 J/m |
| 23°C | ISO 180 | 16to61 kJ/m² | |
| Dart impact | 23°C | ASTM D3763 | 35.3to47.9 J |
| hardness | Test Condition | Test Method | Generic/Generic ASA+PC |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 88.7to110 MPa | |
| Rockwell hardness | 23°C | ASTM D785 | 109to116 |
| Electrical performance | Test Condition | Test Method | Generic/Generic ASA+PC |
|---|---|---|---|
| Volume resistivity | 23°C | IEC 60093 | 1.0E+13到1.0E+15 ohms·cm |
| Surface Resistivity | IEC 60093 | 1.0E+13到1.0E+15 ohms |
| Mechanical properties | Test Condition | Test Method | Generic/Generic ASA+PC |
|---|---|---|---|
| tensile strength | 断裂,23°C | ASTM D638 | 44.0to66.0 MPa |
| bending strength | 23°C | ASTM D790 | 68.0to94.0 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 2120to2760 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 54.6to62.4 MPa |
| bending strength | 屈服,23°C | ASTM D790 | 81.7to95.4 MPa |
| elongation | 屈服,23°C | ISO 527-2 | 2.3to8.7 % |
| 断裂,23°C | ISO 527-2 | 36to80 % | |
| Flexural modulus | 23°C | ISO 178 | 2000to2640 MPa |
| Tensile modulus | 23°C | ASTM D638 | 2540to2720 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 39.0to64.3 MPa |
| Flexural modulus | 23°C | ASTM D790 | 2080to2770 MPa |
| elongation | 屈服,23°C | ASTM D638 | 3.7to6.1 % |
| tensile strength | 屈服,23°C | ASTM D638 | 52.9to65.6 MPa |
| elongation | 断裂,23°C | ASTM D638 | 23to100 % |
| bending strength | 23°C | ISO 178 | 72.8to97.5 MPa |
| flammability | Test Condition | Test Method | Generic/Generic ASA+PC |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 550to960 °C |
| physical property | Test Condition | Test Method | Generic/Generic ASA+PC |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.59to0.70 % |
| MD:23°C | ASTM D955 | 0.50to0.60 % | |
| density | 23°C | ISO 1183 | 1.11to1.20 g/cm³ |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 14to45 g/10min |
| 260°C/5.0kg | ISO 1133 | 19to40 g/10min | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20to0.30 % |
| 23°C,24hr | ASTM D570 | 0.10to0.25 % | |
| 饱和,23°C | ISO 62 | 0.60to1.0 % | |
| density | -- | ASTM D792 | 1.10to1.25 g/cm³ |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 17.0to26.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | Generic/Generic ASA+PC |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 87.7to113 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 102to130 °C | |
| vicat | -- | ASTM D1525 | 104to138 °C |
| Linear coefficient of thermal expansion | TD | ASTME831 | 7.2E-5到7.9E-5 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 98.4to132 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 87.2to122 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.0E-5到8.6E-5 cm/cm/°C |
| MD | ASTME831 | 7.2E-5到7.3E-5 cm/cm/°C | |
| TD | ISO 11359-2 | 7.1E-5到7.8E-5 cm/cm/°C | |
| vicat | -- | ISO 306 | 102to139 °C |