Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.51 g/cm³ |
| Apparent density | | ASTM D1895 | 0.62 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.74 % |
| Water absorption rate | | ASTM D570 | 0.19 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | 40 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ASTM D256 | 15.3 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 14 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 79.9 MPa |
| compressive strength | | ASTM D695 | 184 MPa |
| Tensile modulus | | ASTM D638 | 8710 MPa |
| tensile strength | | ASTM D638 | 50.0 MPa |
| elongation | Break | ASTM D638 | 0.70 % |
| Flexural modulus | | ASTM D790 | 7860 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 3 |
| Volume resistivity | | ASTM D257 | 1.7E+11 ohms·cm |
| dielectric strength | | ASTM D149 | 11 kV/mm |
| dielectric strength | | ASTM D149 | 7.2 kV/mm |
| dielectric constant | | ASTM D150 | 5.50 |
| Dissipation Factor | | ASTM D150 | 0.064 |
| arc resistance | | ASTM D495 | 163 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 173 °C |
| Continuous use temperature | | ASTM D794 | 201 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 4.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.