PPO(PPE)+PS+PP NORYL PPX™ PPX7115F resin
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.988 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 14 g/10min | |
| Melt volume flow rate | ISO 1133 | 12.0 cm³/10min | |
| Shrinkage rate | 内部方法 | 0.60to0.70 % | |
| 内部方法 | 0.60to0.80 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ISO 527-2/50 | 35.0 MPa |
| Break | ASTM D638 | 34.5 MPa | |
| elongation | Yield | ASTM D638 | 8.0 % |
| Break | ASTM D638 | 130 % | |
| Tensile strain | Break | ISO 527-2/50 | 75 % |
| Tensile modulus | ASTM D638 | 1240 MPa | |
| ISO 527-2/1 | 1380 MPa | ||
| tensile strength | Yield | ASTM D638 | 35.9 MPa |
| Flexural modulus | ASTM D790 | 1380 MPa | |
| bending strength | ASTM D790 | 51.7 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 530 J/m | |
| Dart impact | ASTM D3763 | 30.0 J | |
| ASTM D3763 | 37.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 85.0 °C | |
| vicat | ASTM D15256 | 86.7 °C | |
| ISO 306/A50 | 131 °C | ||
| Linear coefficient of thermal expansion | ASTME831 | 1.6E-04 cm/cm/°C | |
| ASTME831 | 9.7E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 113 °C | |
| ISO 75-2/Bf | 116 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.