Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO(PPE)+PS+PP NORYL PPX™ PPX7115F resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL PPX™ PPX7115F resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 530 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 37.0 J |
| -30°C,TotalEnergy | ASTM D3763 | 30.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL PPX™ PPX7115F resin |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 130 % |
| 屈服 | ASTM D638 | 8.0 % | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 51.7 MPa |
| tensile strength | 断裂 | ASTM D638 | 34.5 MPa |
| Tensile modulus | ASTM D638 | 1240 MPa | |
| tensile strength | 屈服 | ASTM D638 | 35.9 MPa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1380 MPa |
| Tensile strain | 断裂 | ISO 527-2/50 | 75 % |
| Tensile modulus | ISO 527-2/1 | 1380 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 35.0 MPa |
| physical property | Test Condition | Test Method | SABIC/NORYL PPX™ PPX7115F resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.60to0.70 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 14 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.60to0.80 % |
| density | ASTM D792 | 0.988 g/cm³ | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 12.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL PPX™ PPX7115F resin |
|---|---|---|---|
| vicat | ISO 306/A50 | 131 °C | |
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 116 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 9.7E-05 cm/cm/°C |
| vicat | ASTM D15256 | 86.7 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.6E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 113 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 85.0 °C |