LDPE SABIC® 2100TN00W
27
- Properties:High toughnessGood peel resistanceExcluding additives. Prod
- Usages:filmLiningBagHeavy-duty thin filmShrink filmIndustrial bags and linersetc
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 0.3 g/10min | |
| density | ISO 1183 | 921 kg/m3 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | ISO 527-3 | 11 Mpa | |
| Breaking stress | ISO 527-3 | 28 Mpa | |
| ISO 527-3 | 23 Mpa | ||
| elongation at break | ISO 527-3 | ＞200 % | |
| ISO 527-3 | ＞500 % | ||
| Elastic modulus | ISO 527-3 | 190 Mpa | |
| ISO 527-3 | 190 Mpa | ||
| coefficient of friction | ASTM D-1894 | 1.0 | |
| Impact strength of cantilever beam gap | ASTM D-4272 | 30 KJ/m | |
| tear strength | ISO 6383-2 | 30 kN/m | |
| ISO 6383-2 | 30 kN/m | ||
| Tensile stress | ISO 527-3 | 11 Mpa |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | ASTM D-1003A | 12 % | |
| transparency | SABIC method | 50 mV | |
| Viscosity | SABIC method | 20 g | |
| Post viscosity | SABIC method | 10 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306 | 93 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.