LDPE 2100TN00W SABIC SAUDI
SABIC®
film、Lining、Bag、Heavy-duty thin film、Shrink film、Industrial bags and liner
High toughness、Good peel resistance、Excluding additives. Prod
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | SABIC SAUDI/2100TN00W |
|---|---|---|---|
| Haze ratio | ASTM D-1003A | 12 % | |
| Post viscosity | SABIC method | 10 g | |
| transparency | SABIC method | 50 mV | |
| Viscosity | SABIC method | 20 g |
| Basic performance | Test Condition | Test Method | SABIC SAUDI/2100TN00W |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 0.3 g/10min |
| density | ISO 1183 | 921 kg/m3 |
| Mechanical properties | Test Condition | Test Method | SABIC SAUDI/2100TN00W |
|---|---|---|---|
| Elastic modulus | MD | ISO 527-3 | 190 Mpa |
| Tensile stress | MD，屈服 | ISO 527-3 | 11 Mpa |
| Impact strength of cantilever beam gap | ASTM D-4272 | 30 KJ/m | |
| Breaking stress | MD | ISO 527-3 | 28 Mpa |
| elongation at break | MD | ISO 527-3 | ＞200 % |
| coefficient of friction | ASTM D-1894 | 1.0 | |
| tear strength | TD | ISO 6383-2 | 30 kN/m |
| Breaking stress | TD | ISO 527-3 | 23 Mpa |
| elongation at break | TD | ISO 527-3 | ＞500 % |
| tear strength | MD | ISO 6383-2 | 30 kN/m |
| Elastic modulus | TD | ISO 527-3 | 190 Mpa |
| Tensile stress | TD，屈服 | ISO 527-3 | 11 Mpa |
| Thermal performance | Test Condition | Test Method | SABIC SAUDI/2100TN00W |
|---|---|---|---|
| vicat | 10N | ISO 306 | 93 °C |