Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 26.0 cm3/10min |
| Shrinkage rate - flow | | 内部方法 | 0.50 到 0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ISO 4589-2 | 21 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2400 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2300 Mpa |
| tensile strength | | ASTM D638 | 53.0 Mpa |
| tensile strength | | ISO 527-2/5 | 45.0 Mpa |
| tensile strength | | ISO 527-2/50 | 50.0 Mpa |
| tensile strength | | ASTM D638 | 43.0 Mpa |
| tensile strength | | ISO 527-2/5, ISO 527-2/50 | 40.0 Mpa |
| elongation | | ASTM D638 | 3.6 % |
| elongation | | ISO 527-2/5, ISO 527-2/50 | 4.0 % |
| elongation | | ASTM D638 | 24 % |
| elongation | | ISO 527-2/5 | 45 % |
| elongation | | ISO 527-2/50 | 20 % |
| Flexural modulus | | ASTM D790 | 2440 Mpa |
| Flexural modulus | | ISO 178 | 2500 Mpa |
| Bending stress | | ISO 178 | 80.0 Mpa |
| Bending stress | | ASTM D790 | 86.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam gap 7 | | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam gap 7 | | ISO 179/1eA | 13 kJ/m² |
| Dart impact equipped with measuring instruments | | ASTM D3763 | 42.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | > 1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | > 1.0E+15 ohms·cm |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| drying time | | | 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Temperature at the rear of the barrel | | | 230 到 245 °C |
| Temperature in the middle of the barrel | | | 250 到 260 °C |
| Temperature at the front of the material cylinder | | | 260 到 270 °C |
| Processing (melt) temperature | | | 250 到 270 °C |
| Temperature | | | 40 到 80 °C |
| Back pressure | | | 0.200 到 0.300 Mpa |
| screw speed | | | 30 到 60 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 116 °C |
| Thermal deformation temperature under load | | ISO 75-2/Bf | 114 °C |
| Thermal deformation temperature under load | | ASTM D648 | 99.0 °C |
| Thermal deformation temperature under load | | ISO 75-2/Ae | 95.0 °C |
| vicat | | ISO 306/B50 | 113 °C |
| vicat | | ISO 306/B120 | 115 °C |
| | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| | ISO 11359-2 | 8.7E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.