Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PTFE NL001 WH8A511 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/NL001 WH8A511 |
|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 42.0 J |
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 10 kJ/m² |
| 23°C | ISO 179/1eA | 13 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/NL001 WH8A511 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 50.0 Mpa |
| Bending stress | -- 5, 6 | ISO 178 | 80.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 20 % |
| Flexural modulus | -- 5 | ISO 178 | 2500 Mpa |
| elongation | 屈服 3 | ASTM D638 | 3.6 % |
| Bending stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 86.0 Mpa |
| Tensile modulus | -- 2 | ASTM D638 | 2400 Mpa |
| tensile strength | 屈服 3 | ASTM D638 | 53.0 Mpa |
| 断裂 | ISO 527-2/5, ISO 527-2/50 | 40.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距 4 | ASTM D790 | 2440 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 45.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2300 Mpa |
| elongation | 断裂 3 | ASTM D638 | 24 % |
| tensile strength | 断裂 3 | ASTM D638 | 43.0 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 45 % |
| 屈服 | ISO 527-2/5, ISO 527-2/50 | 4.0 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/NL001 WH8A511 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/NL001 WH8A511 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 21 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/NL001 WH8A511 |
|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 260°C/5.0 kg | ISO 1133 | 26.0 cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/NL001 WH8A511 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 115 °C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 95.0 °C |
| 横向 : 23 到 80°C | ISO 11359-2 | 8.7E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Bf | 114 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 99.0 °C | |
| vicat | -- | ISO 306/B50 | 113 °C |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 116 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/NL001 WH8A511 |
|---|---|---|---|
| Temperature | 40 到 80 °C | ||
| screw speed | 30 到 60 rpm | ||
| Temperature at the rear of the barrel | 230 到 245 °C | ||
| Processing (melt) temperature | 250 到 270 °C | ||
| Back pressure | 0.200 到 0.300 Mpa | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 260 到 270 °C | ||
| drying time | 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 250 到 260 °C |