PP PPH7060 TOTAI FRANCE

Usages:
Toychipcontainer
Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss	45°，50.0 μm，铸造薄膜45°，50.0 μm，铸造薄膜	ASTM D2457	85
turbidity	50 μm，铸造薄膜50.0 μm，铸造薄膜	ISO 14782	4 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23℃23℃	ISO 180	3.5 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Rockwell hardness	R-ScaleR-Scale	ISO 2039-2	95
Bending modulus		ISO 178	1450 Mpa
Tensile modulus		ISO 527-2	1550 Mpa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature	DSCDSC	ISO 3146	165 °C
Vicat softening temperature	B50--	ISO 306	87 °C
Vicat softening temperature	Vicat softening temperature	A50--	ISO 306/A50	152 °C
Hot deformation temperature	0.45 MPa，Unannealed0.45 MPa，Unannealed	ISO 75-2/B	100 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa，Unannealed1.8 MPa，Unannealed	ISO 75-2/A	55 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	0.905 g/cm³
Apparent density		ISO 1183	0.53 g/cm³
melt mass-flow rate	230℃，2.16kg230℃/2.16 kg	ISO 1133	12 g/10min

film properties	Test Condition	Test Method	Test Result
Elmendorf tear strength	MD：50 μm，铸造薄膜MD : 2.0 mil, Cast Film	ISO 6383-2	10 N
Dart impact	50 μm，铸造薄膜50 μm，铸造薄膜	ISO 7765-1	270 g
Tensile strain	TD，Break，50 μm，铸造薄膜TD : Break, 2.0 mil, Cast Film	ISO 527-3	600 %
	Tensile strain	MD，Break，50 μm，铸造薄膜MD : Break, 2.0 mil, Cast Film	ISO 527-3	500 %
	Tensile strain	Tensile strain	YieldYield	ISO 527-2	10 %
tensile strength	TD，Yield，50 μm，Blown FilmTD : Yield, 2.0 mil, Cast Film	ISO 527-3	23 Mpa
	tensile strength	MD，Yield，50 μm，Blown FilmMD : Yield, 2.0 mil, Cast Film	ISO 527-3	23 Mpa
	tensile strength	tensile strength	YieldYield	ISO 527-2	32 Mpa
film thickness	测试经测试		50 µm
tensile strength	TD，Break，50 μm，Blown Film TD : Break, 2.0 mil, Cast Film	ISO 527-3	34 Mpa
tensile strength	tensile strength	MD，Break，50 μm，Blown Film MD : Break, 2.0 mil, Cast Film	ISO 527-3	44 Mpa
Elmendorf tear strength	TD：50 μm，铸造薄膜TD : 2.0 mil, Cast Film	ISO 6383-2	28 N

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.