Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP PPH7060 TOTAI FRANCE
--
Toy,chip,container
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TOTAI FRANCE/PPH7060 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃23℃ | ISO 180 | 3.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | TOTAI FRANCE/PPH7060 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 1550 Mpa | |
| Rockwell hardness | R 级R 级 | ISO 2039-2 | 95 |
| Flexural modulus | ISO 178 | 1450 Mpa |
| optical performance | Test Condition | Test Method | TOTAI FRANCE/PPH7060 |
|---|---|---|---|
| gloss | 45°，50.0 µm，铸造薄膜45°，50.0 µm，铸造薄膜 | ASTM D2457 | 85 |
| Haze ratio | 50 µm，铸造薄膜50.0 µm，铸造薄膜 | ISO 14782 | 4 % |
| film properties | Test Condition | Test Method | TOTAI FRANCE/PPH7060 |
|---|---|---|---|
| tensile strength | MD，屈服，50 µm，吹塑薄膜MD : Yield, 2.0 mil, Cast Film | ISO 527-3 | 23 Mpa |
| Tensile strain | 屈服屈服 | ISO 527-2 | 10 % |
| Elmendorf tear strength | MD：50 µm，铸造薄膜MD : 2.0 mil, Cast Film | ISO 6383-2 | 10 N |
| tensile strength | MD，断裂，50 µm，吹塑薄膜 MD : Break, 2.0 mil, Cast Film | ISO 527-3 | 44 Mpa |
| TD，屈服，50 µm，吹塑薄膜TD : Yield, 2.0 mil, Cast Film | ISO 527-3 | 23 Mpa | |
| Elmendorf tear strength | TD：50 µm，铸造薄膜TD : 2.0 mil, Cast Film | ISO 6383-2 | 28 N |
| Tensile strain | TD，断裂，50 µm，铸造薄膜TD : Break, 2.0 mil, Cast Film | ISO 527-3 | 600 % |
| MD，断裂，50 µm，铸造薄膜MD : Break, 2.0 mil, Cast Film | ISO 527-3 | 500 % | |
| Dart impact | 50 µm，铸造薄膜50 µm，铸造薄膜 | ISO 7765-1 | 270 g |
| tensile strength | 屈服屈服 | ISO 527-2 | 32 Mpa |
| film thickness | 测试经测试 | 50 µm | |
| tensile strength | TD，断裂，50 µm，吹塑薄膜 TD : Break, 2.0 mil, Cast Film | ISO 527-3 | 34 Mpa |
| physical property | Test Condition | Test Method | TOTAI FRANCE/PPH7060 |
|---|---|---|---|
| melt mass-flow rate | 230℃，2.16kg230℃/2.16 kg | ISO 1133 | 12 g/10min |
| Apparent density | ISO 1183 | 0.53 g/cm³ | |
| density | ISO 1183 | 0.905 g/cm³ |
| Thermal performance | Test Condition | Test Method | TOTAI FRANCE/PPH7060 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa，未退火0.45 MPa，未退火，HDT | ISO 75-2/B | 100 °C |
| vicat | A50-- | ISO 306/A50 | 152 °C |
| Heat distortion temperature | 1.8 MPa，未退火1.8 MPa，未退火，HDT | ISO 75-2/A | 55 °C |
| vicat | B50-- | ISO 306 | 87 °C |
| melting temperature | DSCDSC | ISO 3146 | 165 °C |