Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 2.14to2.16 g/cm³ |
| Apparent density | | JISK6891 | 1.00to1.40 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 10to17 g/10min |
| Water absorption rate | Saturation | ASTM D570 | <0.010 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 60to70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | >95 % |
| UL flame retardant rating | | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | | 2.00E+6到2.50E+7 mPa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | JISK6891 | 25.4to30.4 MPa |
| Heat distortion temperature | | ASTM D621 | 8.00to9.00 % |
| Heat distortion temperature | | ASTM D621 | 2.00to3.00 % |
| Heat distortion temperature | | ASTM D621 | 8.50to9.50 % |
| bending strength | | ASTM D790 | Nobreak |
| elongation | Break | JISK6891 | 350to450 % |
| Flexural modulus | | ASTM D790 | 580to690 MPa |
| Compression Modulus | | ASTM D695 | 490to590 MPa |
| compressive strength | | ASTM D695 | 4.90to5.90 MPa |
| compressive strength | | ASTM D695 | 31.4to33.3 MPa |
| compressive strength | | ASTM D695 | 0.040to0.050 |
| Heat distortion temperature | | ASTM D621 | 2.50to3.00 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 1.2E-04 cm/cm/°C |
| specific heat | | | 1050 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.26 W/m/K |
| melting temperature | | ASTM D4591 | 300to310 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.