PFA NEOFLON™ AP-210 DAIKIN INDUSTRIES, Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./NEOFLON™ AP-210 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 无断裂 |
| hardness | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./NEOFLON™ AP-210 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 60to70 |
| Mechanical properties | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./NEOFLON™ AP-210 |
|---|---|---|---|
| tensile strength | 屈服 | JISK6891 | 25.4to30.4 MPa |
| compressive strength | 1%应变 | ASTM D695 | 4.90to5.90 MPa |
| bending strength | ASTM D790 | Nobreak | |
| Heat distortion temperature | 25°C,14MPa2，HDT | ASTM D621 | 2.50to3.00 % |
| Flexural modulus | ASTM D790 | 580to690 MPa | |
| Compression Modulus | ASTM D695 | 490to590 MPa | |
| Heat distortion temperature | 25°C,14MPa3，HDT | ASTM D621 | 8.00to9.00 % |
| compressive strength | 25%应变 | ASTM D695 | 31.4to33.3 MPa |
| Heat distortion temperature | 100°C,6.9MPa2，HDT | ASTM D621 | 2.00to3.00 % |
| elongation | 断裂 | JISK6891 | 350to450 % |
| Heat distortion temperature | 100°C,6.9MPa3，HDT | ASTM D621 | 8.50to9.50 % |
| compressive strength | 摩擦系数(与钢-静态) | ASTM D695 | 0.040to0.050 |
| flammability | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./NEOFLON™ AP-210 |
|---|---|---|---|
| Limiting Oxygen Index | 1.57mm | ASTM D2863 | >95 % |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./NEOFLON™ AP-210 |
|---|---|---|---|
| melt viscosity | 380°C | 2.00E+6到2.50E+7 mPa·s |
| physical property | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./NEOFLON™ AP-210 |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | <0.010 % |
| density | ASTM D792 | 2.14to2.16 g/cm³ | |
| Apparent density | JISK6891 | 1.00to1.40 g/cm³ | |
| melt mass-flow rate | 372°C/5.0kg | ASTM D1238 | 10to17 g/10min |
| Thermal performance | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./NEOFLON™ AP-210 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：20到100°C | ASTM D696 | 1.2E-04 cm/cm/°C |
| thermal conductivity | ASTMC177 | 0.26 W/m/K | |
| melting temperature | ASTM D4591 | 300to310 °C | |
| specific heat | 1050 J/kg/°C |