PBT LNP™ THERMOCOMP™ WF1003 BK
152
- Properties:wear resistant
- Usages:Electronic and electrical components
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.080 % | |
| Shrinkage rate | ASTM D955 | 0.70 % | |
| ASTM D955 | 1.0 % | ||
| ISO 294-4 | 0.95 % | ||
| ISO 294-4 | 0.75 % | ||
| Water absorption rate | ASTM D570 | 0.090 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 130 Mpa | |
| Tensile modulus | ISO 527-2/1 | 5010 Mpa | |
| tensile strength | ISO 527-2 | 78.0 Mpa | |
| ASTM D638 | 79.8 Mpa | ||
| ISO 527-2 | 76.0 Mpa | ||
| Tensile strain | ISO 527-2 | 3.0 % | |
| ISO 527-2 | 4.0 % | ||
| Flexural modulus | ASTM D790 | 4590 Mpa | |
| ISO 178 | 4710 Mpa | ||
| bending strength | ASTM D790 | 135 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 14 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 46 kJ/m² | |
| Dart impact | ASTM D3763 | 12.2 J | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 4.22 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 201 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.