PBT WF1003 BK SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/WF1003 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 46 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 4.22 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 12.2 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/WF1003 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 5010 Mpa | |
| bending strength | ISO 178 | 130 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 4.0 % |
| Flexural modulus | ISO 178 | 4710 Mpa | |
| bending strength | ASTM D790 | 135 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 3.0 % |
| tensile strength | 断裂 | ASTM D638 | 79.8 Mpa |
| 断裂 | ISO 527-2 | 76.0 Mpa | |
| 屈服 | ISO 527-2 | 78.0 Mpa | |
| Flexural modulus | ASTM D790 | 4590 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/WF1003 BK |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.75 % |
| MD：24小时 | ASTM D955 | 0.70 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.090 % |
| 平衡,23°C,50%RH | ISO 62 | 0.080 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 1.0 % |
| TD:24小时 | ISO 294-4 | 0.95 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/WF1003 BK |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 201 °C |