Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.34 g/cm³ |
| Thickness-LayerCapability | | | 254.0到330.2 µm |
| flammability | Test Condition | Test Method | Test Result |
|---|
| NBSSmokeDensity | | ASTMF814/E662 | Passed |
| NBSSmokeDensity | | ASTMF814/E662 | Passed |
| OSU total heat release | | FAR25.853 | 16.0 kW·min/m² |
| OSU total heat release | | FAR25.853 | 36.0 kW/m² |
| Vertical combustion- | | FAR25.853 | 2.0 sec |
| Heat release- | | FAR25.853 | Passed |
| Flammability - FAA | | FAR25.853 | <5.00 |
| UL flame retardant rating | | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Outgassing | | ASTME595 | -0.10 % |
| Outgassing | | ASTME595 | 0.41 % |
| Outgassing | | ASTME595 | -0.37 % |
| Antifungal properties - Method | | MILSTD-810G | Passed |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2220 MPa |
| tensile strength | | ASTMD638 | 71.7 MPa |
| elongation | | ASTMD638 | 6.0 % |
| Flexural modulus | | ASTMD790 | 2500 MPa |
| shear strength | | ASTMD732 | 57.2 MPa |
| bending strength | | ASTMD790 | 115 MPa |
| Compression Modulus | | ASTMD732 | 1930 MPa |
| compressive strength | | ASTMD695 | 105 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256A | 110 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 610 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTMD149 | 4.3到11 kV/mm |
| dielectric constant | | ASTMD150 | 3.00到3.20 |
| Dissipation Factor | | ASTMD150 | 2.6E-3到2.7E-3 |
| Volume Resistance | | ASTMD257 | 6.0E+13到1.0E+14 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 153 °C |
| Glass Transition Temperature | | DSC | 367 °C |
| | ASTME228 | 6.6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.