PEI Stratasys ULTEM™ 9085 Stratasys
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Stratasys/Stratasys ULTEM™ 9085 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 610 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256A | 110 J/m |
| Supplementary Information | Test Condition | Test Method | Stratasys/Stratasys ULTEM™ 9085 |
|---|---|---|---|
| Outgassing | CollectedVolatileCondensableMaterial(CVCM) | ASTME595 | -0.10 % |
| TotalMassLost(TML) | ASTME595 | 0.41 % | |
| WaterVaporRecovered(WVR) | ASTME595 | -0.37 % | |
| Antifungal activity | 方法 | MILSTD-810G | Passed |
| Mechanical properties | Test Condition | Test Method | Stratasys/Stratasys ULTEM™ 9085 |
|---|---|---|---|
| elongation | 断裂,3.18mm | ASTM D638 | 6.0 % |
| Tensile modulus | 3.18mm | ASTM D638 | 2220 MPa |
| compressive strength | ASTM D695 | 105 MPa | |
| Flexural modulus | ASTM D790 | 2500 MPa | |
| shear strength | 6.35mm | ASTM D732 | 57.2 MPa |
| bending strength | ASTM D790 | 115 MPa | |
| tensile strength | 3.18mm | ASTM D638 | 71.7 MPa |
| Compression Modulus | ASTM D732 | 1930 MPa |
| Electrical performance | Test Condition | Test Method | Stratasys/Stratasys ULTEM™ 9085 |
|---|---|---|---|
| Dissipation Factor | ASTM D150 | 2.6E-3到2.7E-3 | |
| dielectric strength | ASTM D149 | 4.3to11 kV/mm | |
| dielectric constant | ASTM D150 | 3.00to3.20 | |
| Volume resistivity | ASTM D257 | 6.0E+13到1.0E+14 ohms |
| flammability | Test Condition | Test Method | Stratasys/Stratasys ULTEM™ 9085 |
|---|---|---|---|
| UL flame retardant rating | FAA | FAR25.853 | <5.00 |
| UL 94 | V-0 | ||
| NBSSmokeDensity | non-flaming | ASTMF814/E662 | Passed |
| OSU total heat release | 5mintest | FAR25.853 | 36.0 kW/m² |
| NBSSmokeDensity | flaming | ASTMF814/E662 | Passed |
| OSU total heat release | 2mintest | FAR25.853 | 16.0 kW·min/m² |
| UL combustion rating | 1.02到6.35mm，垂直 | FAR25.853 | 2.0 sec |
| exothermic | 1.52mm | FAR25.853 | Passed |
| physical property | Test Condition | Test Method | Stratasys/Stratasys ULTEM™ 9085 |
|---|---|---|---|
| thickness | 层能力 | 254.0to330.2 µm | |
| density | ASTM D792 | 1.34 g/cm³ |
| Thermal performance | Test Condition | Test Method | Stratasys/Stratasys ULTEM™ 9085 |
|---|---|---|---|
| Glass Transition Temperature | DSC | 367 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 153 °C |
| Linear coefficient of thermal expansion | MD | ASTME228 | 6.6E-05 cm/cm/°C |