ABS MALECCA K-095 DENKA JAPAN
14
- Properties:heat-resisting
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | JIS K-6874 | 10 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Izod notch impact strength | ASTM D256/ISO 179 | 78 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 42 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 114 | |
| Flexural modulus | ASTM D790/ISO 178 | 2350 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 74 kg/cm²(MPa)[Lb/in²] | |
| Izod notch impact strength | ASTM D256/ISO 179 | 206 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D-790 | 74 Mpa | |
| Rockwell hardness | ASTM D-785 | 114 R | |
| tensile strength | ASTM D-638 | 42 Mpa | |
| Izod impact strength | ASTM D-256 | 206 J/m | |
| ASTM D-790 | 2350 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| Mold Shrinkage | ASTM D955 | 0.4-0.6 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTM D648/ISO 75 | 100 ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 110 ℃（℉） | |
| JIS K-7206 | 110 °C | ||
| ASTM D-648 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.