ABS K-095 DENKA JAPAN
MALECCA
--
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DENKA JAPAN/K-095 |
|---|---|---|---|
| melt mass-flow rate | 220℃,10kg | JIS K-6874 | 10 g/10min |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/K-095 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 206 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 74 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2350 kg/cm²(MPa)[Lb/in²] | |
| 15mm/min | ASTM D-790 | 2350 Mpa | |
| Rockwell hardness | 23℃ | ASTM D-785 | 114 R |
| tensile strength | ASTM D-638 | 42 Mpa | |
| Rockwell hardness | ASTM D785 | 114 | |
| Impact strength of cantilever beam gap | 1/4＂带缺口23℃ | ASTM D-256 | 206 J/m |
| tensile strength | ASTM D638/ISO 527 | 42 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 15mm/min | ASTM D-790 | 74 Mpa |
| Physical properties | Test Condition | Test Method | DENKA JAPAN/K-095 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.4-0.6 % | |
| density | ASTM D792/ISO 1183 | 1.05 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/K-095 |
|---|---|---|---|
| vicat | 5kg | JIS K-7206 | 110 °C |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 100 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 110 ℃（℉） | |
| Heat distortion temperature | 6.4mm,1.82MPa，HDT | ASTM D-648 | 100 °C |