Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.935 g/cm³ |
| Apparent density | | ISO 60 | 0.38 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 8.0 g/10 min |
| Environmental stress cracking resistance | | ASTM D1693 | 300 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 68 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UV Rating | | ASTM D2565 | 8000 hr |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 18.0 Mpa |
| Tensile strain | | ISO 527-2 | 500 % |
| Flexural modulus | | ISO 178 | 600 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact Strength | | ARM | 180 J/cm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+17 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 66.0 °C |
| brittle temperature | | ISO 974 | -30.0 °C |
| vicat | | ISO 306 | 119 °C |
| melting temperature | | ISO 11357-3 | 118 °C |
| Oxygen induction time | | ISO 11357 | 50 min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices