ABS

ABS TI-500A DIC JAPAN

Properties:
transparentHigh temperature resistan
Usages:
Home appliance componentsAutomotive sector
Compare View Prices

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			日常杂项物品

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate			3.2 g/10min

mechanical properties	Test Method	Test Result
elongation		30 %
tensile strength		47 Mpa
Impact strength of cantilever beam gap		7 kj/mm
Bending modulus		2400 Mpa
bending strength		65 Mpa
Rockwell hardness		85 L
Elongation at Break	ASTM D638/ISO 527	4 %
tensile strength	ASTM D638/ISO 527	64(断裂) kg/cm²(MPa)[Lb/in²]
Rockwell hardness	ASTM D785	R-69
Bending modulus	ASTM D790/ISO 178	3450 kg/cm²(MPa)[Lb/in²]
bending strength	ASTM D790/ISO 178	104 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap	ASTM D256/ISO 179	10 kg·cm/cm(J/M)ft·lb/in

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	HDT		72 °C
Combustibility (rate)		UL 94	HB
Vicat softening temperature		ASTM D1525/ISO R306	85 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
Ambiguity degree	2m/m		2.5 %
Total Light Transmittance	2m/m		91 %
density		ASTM D792/ISO 1183	1.09
Shrinkage rate		ASTM D955	0.3-0.7 %
Water absorption rate		ASTM D570/ISO 62	0.2 %
melt mass-flow rate		ASTM D1238/ISO 1133	2.0 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.