Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS TI-500A DIC JAPAN
--
Home appliance components、Automotive sector
transparent、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DIC JAPAN/TI-500A |
|---|---|---|---|
| melt mass-flow rate | 3.2 g/10min |
| Mechanical properties | Test Condition | Test Method | DIC JAPAN/TI-500A |
|---|---|---|---|
| Impact strength of cantilever beam gap | 7 kj/mm | ||
| bending strength | ASTM D790/ISO 178 | 104 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 10 kg·cm/cm(J/M)ft·lb/in | |
| elongation | 30 % | ||
| Rockwell hardness | 85 L | ||
| Flexural modulus | ASTM D790/ISO 178 | 3450 kg/cm²(MPa)[Lb/in²] | |
| 2400 Mpa | |||
| bending strength | 65 Mpa | ||
| elongation at break | ASTM D638/ISO 527 | 4 % | |
| tensile strength | 47 Mpa | ||
| Rockwell hardness | ASTM D785 | R-69 | |
| tensile strength | ASTM D638/ISO 527 | 64(断裂) kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | DIC JAPAN/TI-500A |
|---|---|---|---|
| characteristic | 日常杂项物品 |
| Physical properties | Test Condition | Test Method | DIC JAPAN/TI-500A |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.3-0.7 % | |
| density | ASTM D792/ISO 1183 | 1.09 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 2.0 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| physical property | Test Condition | Test Method | DIC JAPAN/TI-500A |
|---|---|---|---|
| ambiguity | 2m/m | 2.5 % | |
| Total Light Transmittance | 2m/m | 91 % |
| Thermal performance | Test Condition | Test Method | DIC JAPAN/TI-500A |
|---|---|---|---|
| Heat distortion temperature | HDT | 72 °C | |
| Combustibility (rate) | UL 94 | HB | |
| vicat | ASTM D1525/ISO R306 | 85 ℃（℉） |