Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.08 g/cm³ |
| density | | ISO 1183 | 1.08 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.9 g/10min |
| Melt volume flow rate | | ISO 1133 | 24.0 cm³/10min |
| Shrinkage rate | | ASTM D955 | 0.20to0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.20to0.60 % |
| Water absorption rate | | ASTM D570 | 0.10 % |
| Water absorption rate | | ISO 62 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 70 |
| ball-indentation hardness | | ISO 2039-1 | 168 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.570 |
| refractive index | | ISO 489 | 1.570 |
| transmissivity | | ASTM D1003 | 91.3 % |
| Haze ratio | | ASTM D1003 | 0.30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 21 J/m |
| Impact strength of cantilever beam gap | | ISO 180/A | 2.5 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 1.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3240 MPa |
| Tensile modulus | | ISO 527-2 | 3300 MPa |
| tensile strength | | ASTM D638 | 57.9 MPa |
| tensile strength | | ISO 527-2 | 60.0 MPa |
| elongation | Break | ASTM D638 | 2.1 % |
| Tensile strain | | ISO 527-2 | 2.5 % |
| Flexural modulus | | ASTM D790 | 3100 MPa |
| Flexural modulus | | ISO 178 | 3400 MPa |
| bending strength | | ASTM D790 | 97.2 MPa |
| bending strength | | ISO 178 | 100 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 90.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 80.0 °C |
| vicat | | ASTM D15253 | 106 °C |
| vicat | | ISO 306/B50 | 98.0 °C |
| maximum service temperature | | | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.