Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 27.0 cm3/10min |
| Shrinkage rate | | ISO2577 | 0.55to0.75 % |
| Shrinkage rate | | ISO2577 | 0.55to0.75 % |
| Water absorption rate | | ISO62 | 0.50 % |
| Water absorption rate | | ISO62 | 0.20 % |
| MeltViscosity | | ISO11443-A | 225 Pa·s |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FlameRating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/50 | 62.0 Mpa |
| Tensile strain | | ISO527-2/50 | 5.0 % |
| Tensile strain | | ISO527-2/50 | >50 % |
| Tensile modulus | | ISO527-2/1 | 2450 Mpa |
| Tensile stress | | ISO527-2/50 | 63.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | ISO180 | NoBreak |
| | ISO180 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 225 V |
| Surface Resistivity | | IEC60093 | 1E+16 ohms |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 35 KV/mm |
| | IEC60250 | 3.10 |
| | IEC60250 | 2.80 |
| Dissipation Factor | | IEC60250 | 2.5E-03 |
| Dissipation Factor | | IEC60250 | 0.011 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/B | 127 °C |
| Heat distortion temperature | | ISO75-2/A | 109 °C |
| vicat | | ISO306/B50 | 130 °C |
| vicat | | ISO306/B120 | 132 °C |
| | ISO11359-2 | 7E-05 cm/cm/°C |
| | ISO11359-2 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.