ABS 730EM
0
- Properties:Characteristicsquasi heat resistanceexcellent flow
- Usages:Car rear trimcar partsrearview mirrorscommunication machine parts
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4～0.7 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D-238 | 16 g/10min | |
| ASTM D-238 | 2.5 g/10min | ||
| ASTM D-238 | 24 g/10min | ||
| density | ASTM D-792 | 1.04 g/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D-638 | 480 kg/cm | |
| Impact strength of cantilever beam gap | ASTM D-256 | 23 kg.cm/cm | |
| ASTM D-256 | 25 kg.cm/cm | ||
| elongation at break | ASTM D-638 | 25 % | |
| Rockwell hardness | ASTM D-785 | 108 R SCALE | |
| Flexural modulus | ASTM D-790 | 22000 kg/cm | |
| bending strength | ASTM D-790 | 650 kg/cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D-648 | 92(194) ℃(℉) | |
| ASTM D-648 | 100(212) ℃(℉) | ||
| vicat | ASTM D-1525 | 107(225) ℃(℉) |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.