PA+PPO(PPE) Infino HC-8040
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD792 | 1.10 g/cm³ | |
| melt mass-flow rate | ASTMD1238 | 22 g/10min | |
| Shrinkage rate | ASTM D955 | 0.90to1.2 % | |
| ASTM D955 | 0.90to1.1 % | ||
| ISO 2577 | 0.90to1.1 % | ||
| ISO 2577 | 0.90to1.2 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 114 |
| R-Scale | ASTM D785 | 114 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2000 MPa | |
| ISO 527-2/20 | 2100 MPa | ||
| tensile strength | ASTM D638 | 60.0 MPa | |
| Yield | ISO 527-2/50 | 60.0 MPa | |
| ASTM D638 | 60.0 MPa | ||
| Break | ISO 527-2/50 | 60.0 MPa | |
| elongation | ASTM D638 | 30 % | |
| Break | ISO 527-2/50 | 27 % | |
| Flexural modulus | ASTM D790 | 2200 MPa | |
| ISO 178 | 2100 MPa | ||
| bending strength | ASTM D790 | 84.0 MPa | |
| ISO 178 | 94.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 20 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 200 J/m | |
| ASTM D256 | 180 J/m | ||
| ISO 180/1A | 20 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTME831 | 8E-05 cm/cm/°C | |
| ASTME831 | 9E-05 cm/cm/°C | ||
| ASTME831 | 8.5E-05 cm/cm/°C | ||
| ASTME831 | 1.1E-04 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 108 °C | |
| ISO 75-2/A | 85.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.