'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
EAA PRIMACOR™ 1321 STYRON US
39
- Properties:Heat sealing performanceResistance to stress crachigh strengthHigh toughness
- Usages:Food service sectorFood packagingFood containersMulti layer composite material food packaging
Compare
View PricesTechnical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | 45°，50.8um | ASTM D-2457 | 76 |
| turbidity | 50.8um | ASTM D-1003 | 3.7 % |
| 50.8um | ISO 14782 | 3.7 % | |
| gloss | 45°,50.8μm | ASTM D2457 | 76 |
| turbidity | 50.8μm | ISO 14782 | 3.7 % |
| 50.8μm | ASTM D1003 | 3.7 % |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 2.6 g/10min |
| 190℃/2.16kg | ISO 1133 | 2.6 g/10min | |
| Monomer content | Internal Method | 6.5 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield,Compression Molded | ASTM D-638 | 10 MPa |
| Yield,Compression Molded | ISO 527-2/508 | 10 MPa | |
| Compression Molded，Break | ASTM D-638 | 20.1 MPa | |
| 50.8um，TD,Break | ISO 527-3 | 31.8 MPa | |
| 50.8um，MD,Break | ISO 527-3 | 31.8 MPa | |
| Elongation at Break | 50.8um，TD | ASTM D-882 | 510 % |
| 50.8um，MD | ASTM D-882 | 460 % | |
| 50.8um，MD | ISO 527-3 | 460 % | |
| 50.8um，TD | ISO 527-3 | 510 % | |
| Dart impact | 50.8um | ASTM D-1709B | 410 g |
| 50.8um | ISO 7765-1/B | 410 g | |
| Elmendorf tear strength | 50.8um，MD | ASTM D-1922 | 270 g |
| 50.8um，TD | ASTM D-1922 | 390 g | |
| tensile strength | Compression Molded，Break | ISO 527-2/508 | 20.1 MPa |
| Elongation at Break | Compression Molded | ASTM D-638 | 640 % |
| Compression Molded | ISO 527-2/508 | 640 % | |
| tensile strength | 50.8um，Yield,MD | ASTM D-882 | 11.3 MPa |
| 50.8um，Yield,TD | ASTM D-882 | 11.1 MPa | |
| 50.8um，Yield,MD | ISO 527-3 | 11.3 MPa | |
| 50.8um，Yield,TD | ISO 527-3 | 11.5 MPa | |
| 50.8um，TD,Break | ASTM D-882 | 31.8 MPa | |
| 50.8um，MD,Break | ASTM D-882 | 31.8 MPa | |
| Elmendorf tear strength | 50.8um，MD | ISO 6383-2 | 1200 N |
| 50.8um，TD | ISO 6383-2 | 1700 N | |
| elongation | Break,Compression Molded | ISO 527-2/508 | 640 % |
| Break,Compression Molded4 | ASTM D638 | 640 % | |
| tensile strength | Break,Compression Molded | ISO 527-2/508 | 20.1 Mpa |
| Break,Compression Molded4 | ASTM D638 | 20.1 Mpa | |
| Yield,Compression Molded | ISO 527-2/508 | 10.0 Mpa | |
| Yield,Compression Molded4 | ASTM D638 | 10.0 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | ASTM D-1525 | 88.9 ℃ | |
| ISO 306 | 88.9 ℃ | ||
| Melting temperature | DSC | 103 ℃ | |
| Vicat softening temperature | ASTMD1525 | 88.9 °C | |
| Melting temperature | Internal Method | 103 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-792 | 0.935 g/cm³ | |
| ISO 1183/A | 0.935 g/cm³ | ||
| Content of comonomer | Internal Method | 6.5 % | |
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 2.6 g/10min |
| density | ASTMD792 | 0.935 g/cm³ |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elmendorf tear strength | TD:51μm | ASTM D1922 | 390 g |
| MD:51μm | ISO 6383-2 | 1200 N | |
| TD:51μm | ISO 6383-2 | 1700 N | |
| tensile strength | MD:Yield,51μm | ASTM D882 | 11.3 Mpa |
| TD:Yield,51μm | ASTM D882 | 11.1 Mpa | |
| MD:Yield,51μm | ISO 527-3 | 11.3 Mpa | |
| TD:Yield,51μm | ISO 527-3 | 11.5 Mpa | |
| MD:Break,51μm | ASTMD882 | 31.8 Mpa | |
| TD:Break,51μm | ASTMD882 | 31.8 Mpa | |
| elongation | MD:Break,51μm | ASTMD882 | 460 % |
| TD:Break,51μm | ASTMD882 | 510 % | |
| Dart impact | 51μm | ASTMD1709B | 410 g |
| Elmendorf tear strength | MD:51μm | ASTM D1922 | 270 g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.