Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EAA 1321 STYRON US
PRIMACOR™
Food service sector、Food packaging、Food containers、Multi layer composite mat
Heat sealing performance、Resistance to stress crac、high strength、High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | STYRON US/1321 |
|---|---|---|---|
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 390 g |
| tensile strength | TD:屈服,51µm | ASTM D882 | 11.1 Mpa |
| Dart impact | 51µm | ASTMD1709B | 410 g |
| elongation | TD:断裂,51µm | ASTMD882 | 510 % |
| tensile strength | MD:断裂,51µm | ASTMD882 | 31.8 Mpa |
| MD:屈服,51µm | ASTM D882 | 11.3 Mpa | |
| elongation | MD:断裂,51µm | ASTMD882 | 460 % |
| Elmendorf tear strength | MD:51µm | ISO 6383-2 | 1200 N |
| tensile strength | TD:屈服,51µm | ISO 527-3 | 11.5 Mpa |
| Elmendorf tear strength | TD:51µm | ISO 6383-2 | 1700 N |
| tensile strength | TD:断裂,51µm | ASTMD882 | 31.8 Mpa |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 270 g |
| tensile strength | MD:屈服,51µm | ISO 527-3 | 11.3 Mpa |
| Basic performance | Test Condition | Test Method | STYRON US/1321 |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 2.6 g/10min |
| Monomer content | Internal Method | 6.5 % | |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 2.6 g/10min |
| Mechanical properties | Test Condition | Test Method | STYRON US/1321 |
|---|---|---|---|
| tensile strength | 50.8um，TD,断裂 | ASTM D-882 | 31.8 MPa |
| 屈服,模压成型 | ISO 527-2/508 | 10.0 Mpa | |
| 50.8um，屈服,MD | ASTM D-882 | 11.3 MPa | |
| elongation | 断裂,模压成型 | ISO 527-2/508 | 640 % |
| elongation at break | Compression Molded | ISO 527-2/508 | 640 % |
| 50.8um，TD | ASTM D-882 | 510 % | |
| tensile strength | 屈服,Compression Molded | ISO 527-2/508 | 10 MPa |
| 50.8um，屈服,TD | ISO 527-3 | 11.5 MPa | |
| Compression Molded，断裂 | ASTM D-638 | 20.1 MPa | |
| 50.8um，MD,断裂 | ASTM D-882 | 31.8 MPa | |
| Elmendorf tear strength | 50.8um，MD | ISO 6383-2 | 1200 N |
| elongation at break | 50.8um，TD | ISO 527-3 | 510 % |
| Elmendorf tear strength | 50.8um，TD | ASTM D-1922 | 390 g |
| tensile strength | 断裂,模压成型4 | ASTM D638 | 20.1 Mpa |
| 50.8um，TD,断裂 | ISO 527-3 | 31.8 MPa | |
| elongation at break | Compression Molded | ASTM D-638 | 640 % |
| Dart impact | 50.8um | ASTM D-1709B | 410 g |
| tensile strength | 断裂,模压成型 | ISO 527-2/508 | 20.1 Mpa |
| 屈服,Compression Molded | ASTM D-638 | 10 MPa | |
| 50.8um，屈服,TD | ASTM D-882 | 11.1 MPa | |
| 50.8um，屈服,MD | ISO 527-3 | 11.3 MPa | |
| Compression Molded，断裂 | ISO 527-2/508 | 20.1 MPa | |
| elongation at break | 50.8um，MD | ASTM D-882 | 460 % |
| Elmendorf tear strength | 50.8um，MD | ASTM D-1922 | 270 g |
| elongation at break | 50.8um，MD | ISO 527-3 | 460 % |
| Elmendorf tear strength | 50.8um，TD | ISO 6383-2 | 1700 N |
| tensile strength | 50.8um，MD,断裂 | ISO 527-3 | 31.8 MPa |
| elongation | 断裂,模压成型4 | ASTM D638 | 640 % |
| Dart impact | 50.8um | ISO 7765-1/B | 410 g |
| tensile strength | 屈服,模压成型4 | ASTM D638 | 10.0 Mpa |
| optical performance | Test Condition | Test Method | STYRON US/1321 |
|---|---|---|---|
| Haze ratio | 50.8um | ASTM D-1003 | 3.7 % |
| gloss | 45°,50.8µm | ASTM D2457 | 76 |
| Haze ratio | 50.8um | ISO 14782 | 3.7 % |
| 50.8µm | ISO 14782 | 3.7 % | |
| 50.8µm | ASTM D1003 | 3.7 % | |
| gloss | 45°，50.8um | ASTM D-2457 | 76 |
| physical property | Test Condition | Test Method | STYRON US/1321 |
|---|---|---|---|
| density | ASTM D-792 | 0.935 g/cm³ | |
| Content of comonomer | 内部方法 | 6.5 % | |
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 2.6 g/10min |
| density | ASTMD792 | 0.935 g/cm³ | |
| ISO 1183/A | 0.935 g/cm³ |
| Thermal performance | Test Condition | Test Method | STYRON US/1321 |
|---|---|---|---|
| melting temperature | 内部方法 | 103 °C | |
| vicat | ASTM D-1525 | 88.9 ℃ | |
| ISO 306 | 88.9 ℃ | ||
| melting temperature | DSC | 103 ℃ | |
| vicat | ASTMD1525 | 88.9 °C |