Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.57to1.61 g/cm³ |
| density | | ASTM D792 | 1.57to1.61 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 54to60 |
| Shore hardness | | ASTM D2240 | 67to73 |
| Shore hardness | | ASTM D2240 | 67to73 |
| Shore hardness | | ASTM D2240 | 54to60 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 51 % |
| Limiting Oxygen Index | | ASTM D2863 | 51 % |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 17.9 MPa |
| tensile strength | | ASTM D412 | 15.9 MPa |
| elongation | | ASTM D412 | 210 % |
| elongation | | ASTM D412 | 190 % |
| tensile strength | | ASTM D412 | 17.9 MPa |
| tensile strength | | ASTM D412 | 15.9 MPa |
| elongation | | ASTM D412 | 210 % |
| elongation | | ASTM D412 | 190 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Change rate of tensile strength in air | | UL Unspecified | -1.0 % |
| elongation at break | | UL Unspecified | -7.0 % |
| elongation at break | | UL Unspecified | -7.0 % |
| Change rate of tensile strength in air | | UL Unspecified | -1.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150 | 3.35 |
| Dissipation Factor | | ASTM D150 | 0.014 |
| dielectric constant | | ASTM D150 | 3.35 |
| Dissipation Factor | | ASTM D150 | 0.014 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -4.00 °C |
| brittle temperature | | ASTM D746 | -4.00 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.