PC TARFLON™ IR2200
709
- Properties:Low viscosityHigh mobility
- Usages:Thin walled products
- Certificates:RoHSFDATDS
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Total Light Transmittance | ASTM D-1003 | 85-89 % |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.5-0.7 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 (ASTM D-1238) | 12 g/10min | |
| density | ASTM D-792 | 1.2 g/cm | |
| Water absorption rate | ASTM D-570 | 0.23 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 (ASTM D-256) | 70 KJ/m | |
| Flexural modulus | ISO 178 (ASTM D-790) | 2350 Mpa | |
| Taber abraser | ASTM D-1044 | 12 mg | |
| tensile strength | ISO R-527 (ASTM D-638) | 64 Mpa | |
| bending strength | ISO 178 (ASTM D-790) | 93 Mpa | |
| Tensile modulus | ISO R-527 (ASTM D-638) | 2300 Mpa | |
| Rockwell hardness | ISO 2039-2 (ASTM D-785) | 120 R | |
| tensile strength | ISO R-527 (ASTM D-638) | 68 Mpa | |
| elongation at break | ISO R-527 (ASTM D-638) | 115 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306 | 148 °C | |
| combustibility | UL -94 | V-2 | |
| Linear coefficient of thermal expansion | ASTM D-696 (ASTM D-695) | 6.5 ×10 | |
| Heat distortion temperature | ISO 75 (ASTM D-648) | 132 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.