PC IR2200 FIPC TAIWAN
TARFLON™
Thin walled products
Low viscosity、High mobility
RoHS
FDA
TDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | FIPC TAIWAN/IR2200 |
|---|---|---|---|
| melt mass-flow rate | 300℃ 1.2kg | ISO 1133 (ASTM D-1238) | 12 g/10min |
| Water absorption rate | 23℃水中24h | ASTM D-570 | 0.23 % |
| density | ASTM D-792 | 1.2 g/cm |
| Mechanical properties | Test Condition | Test Method | FIPC TAIWAN/IR2200 |
|---|---|---|---|
| tensile strength | 断裂 | ISO R-527 (ASTM D-638) | 68 Mpa |
| bending strength | ISO 178 (ASTM D-790) | 93 Mpa | |
| Impact strength of cantilever beam gap | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 70 KJ/m |
| Taber abraser | 1,000round | ASTM D-1044 | 12 mg |
| elongation at break | ISO R-527 (ASTM D-638) | 115 % | |
| tensile strength | 屈服 | ISO R-527 (ASTM D-638) | 64 Mpa |
| Flexural modulus | ISO 178 (ASTM D-790) | 2350 Mpa | |
| Tensile modulus | ISO R-527 (ASTM D-638) | 2300 Mpa | |
| Rockwell hardness | ISO 2039-2 (ASTM D-785) | 120 R |
| processability | Test Condition | Test Method | FIPC TAIWAN/IR2200 |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.5-0.7 % |
| physical property | Test Condition | Test Method | FIPC TAIWAN/IR2200 |
|---|---|---|---|
| Total Light Transmittance | 3mm厚 | ASTM D-1003 | 85-89 % |
| Thermal performance | Test Condition | Test Method | FIPC TAIWAN/IR2200 |
|---|---|---|---|
| Heat distortion temperature | 1.8Mpa 18.6kg/cm，HDT | ISO 75 (ASTM D-648) | 132 °C |
| vicat | ISO 306 | 148 °C | |
| combustibility | 1.47mm厚 | UL -94 | V-2 |
| Linear coefficient of thermal expansion | ASTM D-696 (ASTM D-695) | 6.5 ×10 |