AES+PC UMG ALLOY® CZ900 UMG JAPAN
0
- Properties:Thermal performance
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| 线性热膨胀系数 | MD | ISO11359-2 | 8E-05 cm/cm/°C |
| 密度 | 23°C | ISO1183 | 1.11 g/cm³ |
| 熔体体积流动速率 | 230°C/10.0kg | ISO1133 | 12.0 cm³/10min |
| 收缩率 | MD：23°C | ISO294-4 | 0.60到0.80 % |
| 洛氏硬度 | R计秤,23°C | ISO2039-2 | 102 |
| 拉伸模量 | 23°C | ISO527-2 | 2100 MPa |
| 拉伸应力 | 23°C | ISO527-2 | 51.0 MPa |
| 弯曲模量 | 23°C | ISO178 | 2300 MPa |
| 弯曲应力 | 23°C | ISO178 | 78.0 MPa |
| 简支梁缺口冲击强度 | -30°C | ISO179 | 12 kJ/m² |
| 23°C | ISO179 | 48 kJ/m² | |
| 热变形温度 | 1.8MPa,未退火 | ISO75-2/Af | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.