AES+PC UMG ALLOY® CZ900 UMG JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | UMG JAPAN/UMG ALLOY® CZ900 | |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.11 g/cm³ |
| Tensile modulus | 23°C | ISO 527-2 | 2100 MPa |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| Melt volume flow rate | 230°C/10.0kg | ISO 1133 | 12.0 cm³/10min |
| Flexural modulus | 23°C | ISO 178 | 2300 MPa |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 12 kJ/m² |
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.60to0.80 % |
| tensile strength | 23°C | ISO 527-2 | 51.0 MPa |
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 102 |
| bending strength | 23°C | ISO 178 | 78.0 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 48 kJ/m² |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 100 °C |