Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Resin | | 100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:22 |
| Thermosetting components | | | 12 hr |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.11to1.15 g/cm³ |
| Viscosity | | | 1.1to1.5 Pa·s |
| Curing Time | | | 6.0to8.0 hr |
| STORAGE STABILITY | | | 20to25 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 7619 | 83to89 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compression stress | | ISO 604 | 100to120 MPa |
| Flexural modulus | | ISO 178 | 3000to3600 MPa |
| bending strength | | ISO 178 | 118to138 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 12to28 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | DSC | 97.0 °C |
| Heat distortion temperature | | ISO 75-2/B | 96.0to102 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.