Epoxy Ebalta AH 110 / TGS Ebalta Kunststoff GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta AH 110 / TGS |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 12to28 kJ/m² |
| hardness | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta AH 110 / TGS |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 7619 | 83to89 |
| Mechanical properties | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta AH 110 / TGS |
|---|---|---|---|
| compression stress | ISO 604 | 100to120 MPa | |
| Flexural modulus | ISO 178 | 3000to3600 MPa | |
| bending strength | ISO 178 | 118to138 MPa |
| thermosetting | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta AH 110 / TGS |
|---|---|---|---|
| Thermosetting components | 按重量计算的混合比 | 100 | |
| 硬化法 | 按重量计算的混合比:22 | ||
| 后固化时间(80°C) | 12 hr |
| Uncured Properties | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta AH 110 / TGS |
|---|---|---|---|
| Viscosity | 25°C | 1.1to1.5 Pa·s | |
| STORAGE STABILITY | 20°C | 20to25 min | |
| density | 20°C | 1.11to1.15 g/cm³ | |
| Curing Time | 20°C | 6.0to8.0 hr |
| Thermal performance | Test Condition | Test Method | Ebalta Kunststoff GmbH/Ebalta AH 110 / TGS |
|---|---|---|---|
| Glass Transition Temperature | DSC | 97.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 96.0to102 °C |