Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.70 g/cm³ |
| Apparent density | | ISO 60 | 0.74 g/cm³ |
| Shrinkage rate | | ISO 2577 | 0.20 % |
| Water absorption rate | | ISO 62 | 12.0 mg |
| Shrinkage rate | | ISO 2577 | 0.050 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Compression molding pressure | | | >15.0 MPa |
| Compression molding temperature | | | 160to190 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 210 MPa |
| compression stress | | ISO 604 | 250 MPa |
| Tensile modulus | | ISO 527-2/1 | 16000 MPa |
| tensile strength | | ISO 527-2/5 | 100 MPa |
| Flexural modulus | | ISO 178 | 16000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 16 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+11 ohms |
| Volume resistivity | | IEC 60093 | 1E+12 ohms·cm |
| dielectric strength | | IEC 60243-1 | 33 kV/mm |
| relative permittivity | | IEC 60250 | 6.00 |
| Dissipation Factor | | IEC 60250 | 0.050 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/C | 175 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.